沙伯基础SABIC LNP COLORCOMP DX06407 PC 

Material Notes: LNP COLORCOMP DX06407 is an unfilled Polycarbonate. Added features of this material include: Easy Molding, Mold Release, Healthcare

Physical Properties Metric English Comments

Specific Gravity 1.20 g/cc 1.20 g/cc ASTM D792

Density 1.20 g/cc 0.0434 lb/in³ ASTM D792

Linear Mold Shrinkage, Flow 0.00700 - 0.00900 cm/cm 0.00700 - 0.00900 in/in 24HRS; ASTM D955

Linear Mold Shrinkage, Transverse 0.0100 - 0.0300 cm/cm 0.0100 - 0.0300 in/in 24 HRS; ASTM D955

Mechanical Properties Metric English Comments

Tensile Strength at Break 54.0 MPa 7830 psi 5 mm/min; ISO 527

  58.0 MPa 8410 psi 5 mm/min; ASTM D638

Tensile Strength, Yield 63.0 MPa 9140 psi 5 mm/min; ASTM D638

  65.0 MPa 9430 psi 5 mm/min; ISO 527

Elongation at Break 94.0 % 94.0 % 5 mm/min; ASTM D638

  104 % 104 % 5 mm/min; ISO 527

Elongation at Yield 6.20 % 6.20 % 5 mm/min; ASTM D638

  6.30 % 6.30 % 5 mm/min; ISO 527

Tensile Modulus 2.30 GPa 334 ksi 1 mm/min; ISO 527

  2.34 GPa 339 ksi 5 mm/min; ASTM D638

Flexural Strength 91.0 MPa 13200 psi ISO 178

Flexural Modulus 2.29 GPa 332 ksi 2 mm/min; ISO 178

  2.40 GPa 348 ksi 1.3 mm/min, 50 mm span; ASTM D790

Izod Impact, Notched 7.81 J/cm 14.6 ft-lb/in ASTM D256

Izod Impact, Unnotched 13.1 J/cm 24.5 ft-lb/in ASTM D4812

Izod Impact, Notched (ISO) 9.00 kJ/m² 4.28 ft-lb/in² 80*10*4; ISO 180/1A

Izod Impact, Unnotched (ISO) 224 kJ/m² 107 ft-lb/in² 80*10*4; ISO 180/1U

Impact Test 69.0 J 50.9 ft-lb Multiaxial Impact; ISO 6603

Instrumented Impact Total Energy 63.0 J 46.5 ft-lb ASTM D3763